ΔfH°gas (kJ/mol): |
849.4 [4] |
|
ΔfH°solid (kJ/mol): |
0.0 [4] |
|
ΔfH°fusion (kJ/mol): |
52.31 [4] |
|
ΔfH°vaporization (kJ/mol): |
824±21 [1] |
|
|
S°gas (J/mol·K): |
174.0 [4] |
|
S°solid (J/mol·K): |
32.6 [4] |
|
|
ΔfG°gas (kJ/mol): |
807.1 [4] |
|
|
Cp (gas) (J/mol·K): |
21.3 (25 °C) [4] |
|
Cp (solid) (J/mol·K): |
26.1617 (20 °C) [2]
24.27 (25 °C) [4]
25.2384 (100 °C) [2]
26.008 (500 °C) [2] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
4.5 (20 °C) [2]
4.5 (25 °C) [4]
4.6 (100 °C) [2]
4.6 (500 °C) [2]
4.6 (1000 °C) [2]
5.4 (2000 °C) [2]
6.6 (3000 °C) [2] |
|