ΔfH°gas (kJ/mol): |
159.3 (monoatomic) [5]
215.9 (Li2) [5] |
|
ΔfH°solid (kJ/mol): |
0.0 [5] |
|
ΔfH°fusion (kJ/mol): |
2.93 [2]
3.00 [5] |
|
ΔfH°vaporization (kJ/mol): |
148 [2] |
|
|
S°gas (J/mol·K): |
138.8 [5]
197.0 (Li2) [5] |
|
S°solid (J/mol·K): |
29.1 [5] |
|
|
ΔfG°gas (kJ/mol): |
126.6 (Li) [5]
174.4 (Li2) [5] |
|
|
Cp (gas) (J/mol·K): |
20.8 (monoatomic, 25 °C) [5]
36.1 (Li2, 25 °C) [5] |
|
Cp (solid) (J/mol·K): |
22.921 [3]
24.860 (monoatomic, 25 °C) [5] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
46 (25 °C) [5] |