ΔH°atomization (kJ/mol): |
326 |
|
ΔfH°gas (kJ/mol): |
329.7 (Monoatomic) [3] |
|
ΔfH°fusion (kJ/mol): |
10.71 [3] |
|
ΔfH°vaporization (kJ/mol): |
294 [3] |
|
|
S°gas (J/mol·K): |
164.6 [5] |
|
S°solid (J/mol·K): |
28.3 [5] |
|
|
ΔfG°gas (kJ/mol): |
289.4 [5] |
|
ΔfG°solid (kJ/mol): |
0 [2] |
|
|
Cp (solid) (J/mol·K): |
24.167 (20 °C) [4]
25.184 (100 °C) [4]
26.426 (200 °C) [4]
27.781 (300 °C) [4]
29.023 (400 °C) [4] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
22.5 (20 °C) [4]
23.9 (100 °C) [4]
24.3 (200 °C) [4]
25.3 (300 °C) [4]
26.5 (400 °C) [4] |
|