ΔfH°gas (kJ/mol): |
514.2 [6] |
|
ΔfH°solid (kJ/mol): |
0.0 [6] |
|
ΔfH°fusion (kJ/mol): |
17.5 [1]
21.50 [6] |
|
ΔfH°vaporization (kJ/mol): |
459.7 [1] |
|
|
S°gas (J/mol·K): |
182.3 [6] |
|
S°solid (J/mol·K): |
28.9 [6] |
|
|
ΔfG°gas (kJ/mol): |
754.4 [6] |
|
|
Cp (gas) (J/mol·K): |
26.0 (25 °C) [6] |
|
Cp (solid) (J/mol·K): |
25.159 (20 °C) [4]
24.89 (25 °C) [6]
25.799 (100 °C) [4]
28.997 (500 °C) [4]
30.703 (700 °C) [4]
32.409 (900 °C) [4] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
8.4 (25 °C) [6]
8.3 (100 °C) [4]
9.6 (500 °C) [4]
10.4 (900 °C) [4] |
|