ΔfH°gas (kJ/mol): |
473.0 [6] |
|
ΔfH°solid (kJ/mol): |
0.0 [6] |
|
ΔfH°fusion (kJ/mol): |
18.8 [3]
14.15 [6] |
|
ΔfH°vaporization (kJ/mol): |
425±11 [3] |
|
|
S°gas (J/mol·K): |
180.3 [6] |
|
S°solid (J/mol·K): |
30.7 [6] |
|
|
ΔfG°gas (kJ/mol): |
428.4 [6] |
|
|
Cp (gas) (J/mol·K): |
24.4 (25 °C) [6] |
|
Cp (solid) (J/mol·K): |
38.543 (20 °C) [4]
25.060 (25 °C) [6]
40.110 (100 °C) [4]
42.303 (200 °C) [4]
46.063 (400 °C) [4]
47.317 (600 °C) [4]
50.764 (800 °C) [4] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
8.8 (20 °C) [4]
8.6 (25 °C) [6]
8.8 (100 °C) [4]
9.1 (200 °C) [4]
9.4 (400 °C) [4]
9.7 (600 °C) [4]
9.9 (800 °C) [4] |
|