ΔfH°gas (kJ/mol): |
301.2 (gray) [5] |
|
ΔfH°solid (kJ/mol): |
0.0 (white) [5]
-2.1 (gray) [5] |
|
ΔfH°fusion (kJ/mol): |
7.07 [1] |
|
ΔfH°vaporization (kJ/mol): |
296 [1] |
|
|
S°gas (J/mol·K): |
168.5 (gray) [5] |
|
S°solid (J/mol·K): |
51.2 (white) [5]
44.1 (gray) [5] |
|
|
ΔfG°gas (kJ/mol): |
266.2 (gray) [5] |
|
ΔfG°solid (kJ/mol): |
0.1 (gray) [5] |
|
|
Cp (gas) (J/mol·K): |
21.3 (gray, 25 °C) [5] |
|
Cp (solid) (J/mol·K): |
26.2342 (20 °C) [3]
27.112 (white, 25 °C) [5]
25.8 (gray, 25 °C) [5]
28.2217 (100 °C) [3]
30.7060 (200 °C) [3] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
23.5 (20 °C) [3]
22.0 (25 °C) [5]
23.8 (100 °C) [3]
24.2 (200 °C) [3] |
|