ΔfH°gas (kJ/mol): |
782.0 (monoatomic) [4] |
|
ΔfH°solid (kJ/mol): |
0.0 [4] |
|
ΔfH°fusion (kJ/mol): |
24.7 [1]
36.57 [4] |
|
ΔfH°vaporization (kJ/mol): |
758.2 [1] |
|
|
S°gas (J/mol·K): |
185.2 [4] |
|
S°solid (J/mol·K): |
41.5 [4] |
|
|
ΔfG°gas (kJ/mol): |
739.3 [4] |
|
ΔfG°solid (kJ/mol): |
20.9 (25 °C) [4] |
|
|
Cp (solid) (J/mol·K): |
24.8413 (20 °C) [2]
25.36 (25 °C) [4]
26.6590 (100 °C) [2]
27.1891 (500 °C) [2]
30.0670 (1500 °C) [2]
42.1091 (2500 °C) [2] |
|
|
|
Coeff. of linear thermal expansion (106 K-1): |
6.5 (20 °C) [2]
6.3 (25 °C) [4]
6.5 (100 °C) [2]
6.6 (500 °C) [2] |
|